EN 95MnWCr5 low alloyed tool steel plate
Delivery term:The date of payment from buyers deliver within days- Price:
Negotiable
- minimum:
- Total supply:
- Delivery term:
The date of payment from buyers deliver within days
- seat:
Beijing
- Validity to:
Long-term effective
- Last update:
2017-10-22 22:22
- Browse the number:
107
Company Profile
- Shanghai Bozhong Metal Group Co. Ltd By certification [File Integrity]
-
Contact:
bozhong(Ms.)
- Telephone:
-
Area:
Beijing
-
Address:
BUILDING 32#, NO. 518, XINZHUAN ROAD, SONGJIANG, Shanghai, Shanghai, China (201612)
- Website: http://bozhong.tshirtsontour.com/
Product details
Model Number: ZXL107
Brand Name: Baosteel, TISCO
Key Specifications/Special Features:
DescriptionThis alloy is one of the cold work, oil hardening type tool steels, relatively inexpensive containing small amounts of manganeseTungsten and chromiumHardening by oil quench minimizes distortion and crackingApplicationsApplications include short run tooling for blanking dies, cold forming dies and cutting tools operating at ambient temperatureFor working tools, cutting blades, sizing and stamping toolsPhysical properties (average values) at ambient temperature
Density [g/cm3]: 8.0
Thermal conductivity [W/m.K]: 30.0
Chemical composition ( in weight%)
C: 1.43
Si: 0.23
Mn: 0.30
Cr: 0.35
V: 0.25
W: 3.05
Soft annealing
Heat to 720 to 750°C, cool slowly in furnace, this will produce a maximum Brinell hardness of 270
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 650°C, holding for 1-2 hours at heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden from temperature of 800 to 830°C followed by water quenching, hardness after quenching is 66 HRC
Tempering
Tempering temperature: 100 to 250°C
Forging
Hot forming temperature: 1050 to 850°C
Specifications:
Grades: EN 95MnWCr5
Standards: DIN, GB, EN, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy packing or as customer’s requirements
Delivery: 7-20 days after received deposit of T/T
Density [g/cm3]: 8.0
Thermal conductivity [W/m.K]: 30.0
Chemical composition ( in weight%)
C: 1.43
Si: 0.23
Mn: 0.30
Cr: 0.35
V: 0.25
W: 3.05
Soft annealing
Heat to 720 to 750°C, cool slowly in furnace, this will produce a maximum Brinell hardness of 270
Stress relieving
Stress relieving to remove machining stresses should be carried out by heating to approx 650°C, holding for 1-2 hours at heat, followed by air cooling
This operation is performed to reduce distortion during heat treatment
Hardening
Harden from temperature of 800 to 830°C followed by water quenching, hardness after quenching is 66 HRC
Tempering
Tempering temperature: 100 to 250°C
Forging
Hot forming temperature: 1050 to 850°C
Specifications:
Grades: EN 95MnWCr5
Standards: DIN, GB, EN, AISI
Length: 1500-6000mm
Width: 100-1250mm
Thickness: 0.3-200mm
Certification: ISO
Technical treatment: cold-rolled and hot-rolled
Packing and delivery
Packing: standard export seaworthy packing or as customer’s requirements
Delivery: 7-20 days after received deposit of T/T
Shipping Information:
- FOB Port: Shanghai
- Lead Time: 7 - 15 days
- Dimensions per Unit: 6 × 2 × 0.2 Meters
- Weight per Unit: 20 Kilograms
- Units per Export Carton: 5
- Export Carton Dimensions L/W/H: 6 × 2 × 0.2 Meters
- Export Carton Weight: 5 Tons (US)
Main Export Markets:
- Asia
- Australasia
- Central/South America
- Eastern Europe
- Mid East/Africa
- North America
- Western Europe
New Products
-
Plastic Bevel Gear
price: Negotiable
-
528 Eggs Electric Incubator
price: Negotiable
-
Strong waterproof IP67 40mm 4Ohm 3W square speaker
price: Negotiable
-
Railway Aluminum Coil
price: Negotiable
-
Compact Pressure Transducer
price: Negotiable
-
Conventional Rotary Drilling Rig
price: Negotiable